Adakah Inconel 600 keluli tahan karat?

Adakah Inconel 600 keluli tahan karat?

 

Komposisi Inconel

Inconel Unsur (% mengikut jisim)
Ni Cr Fe Mo Nb Co Mn Cu Al Ti Si C S P B
600 72.0 14.0–17.0 6.0–10.0       1.0 0.5     0.5 0.15 0.015    
617 44.2–56.0 20.0–24.0 3.0 8.0–10.0   10.0–15.0 0.5 0.5 0.8–1.5 0.6 0.5 0.15 0.015 0.015 0.006
625 58.0 20.0–23.0 5.0 8.0–10.0 3.15–4.15 1.0 0.5   0.4 0.4 0.5 0.1 0.015 0.015  
690 59.5 30 9.2       0.35 0.01 0.02   0.35 0.019 0.003    
718 50.0–55.0 17.0–21.0 seimbang 2.8–3.3 4.75–5.5 1.0 0.35 0.2–0.8 0.65–1.15 0.3 0.35 0.08 0.015 0.015 0.006
X-750 70.0 14.0–17.0 5.0–9.0   0.7–1.2 1.0 1.0 0.5 0.4–1.0 2.25–2.75 0.5 0.08 0.01  

Is Inconel 600 a stainless steel?Is Inconel 600 a stainless steel?

 

Aloi Inconel

Aloi inconel termasuk:

Inconel 600: Penyelesaian pepejal diperkukuh

Inconel 601

Inconel 625: Tahan asid, kebolehkimpalan yang baik. Versi LCF biasanya digunakan dalam belos.

Inconel 690: Kandungan kobalt rendah untuk aplikasi nuklear, dan kerintangan rendah

Inconel 713C: Pemendakan boleh mengeras aloi tuangan asas nikel-kromium

Inconel 718: Gamma dwi perdana diperkukuh dengan kebolehkimpalan yang baik

Inconel 751: Peningkatan kandungan aluminium untuk kekuatan pecah yang lebih baik dalam julat 1600 darjah F

Inconel 792: Peningkatan kandungan aluminium untuk sifat kakisan suhu tinggi yang dipertingkatkan, digunakan terutamanya dalam turbin gas

Gred Setara Inconel

STANDARD WERKSTOFF NR. UNS GOST AFNOR JIS BS EN ATAU
Inconel 600 2.4816 N06600 МНЖМц 28-2,5-1,5 NC15FE11M NCF 600 NA 13 NiCr15Fe ЭИ868
Inconel 601 2.4851 N06601 XH60BT NC23FeA NCF 601 NA 49 NiCr23Fe ЭИ868
Inconel 617 2.4663 N06617            
Inconel 625 2.4856 N06625 ХН75МБТЮ NC22DNB4M NCF 625 NA 21 NiCr22Mo9Nb ЭИ602
Inconel 690 2.4642 N06690            
Inconel 718 2.4668 N07718            
Inconel 725 - N07725            
Inconel X-750 2.4669 N07750            

Takat Lebur Inconel, Ketumpatan dan Kekuatan Tegangan

  Ketumpatan Takat lebur Kekuatan Tegangan Kekuatan Hasil (0.2%Offset) Pemanjangan
600 8.47 g/cm3 1413 darjah (2580 darjah F) Psi – 95,000 , MPa – 655 Psi – 45,000 , MPa – 310 40 %
601 8.1 g/cm3 1411 darjah (2571 darjah F) Psi – 80,000 , MPa – 550 Psi – 30,000 , MPa – 205 30 %
617 8.3g/cm³ 1363 darjah Lebih besar daripada atau sama dengan 485 MPa Lebih besar daripada atau sama dengan 275 MPa 25 %
625 8.4 g/cm3 1350 darjah (2460 darjah F) Psi – 135,000 , MPa – 930 Psi – 75,000 , MPa – 517 42.5 %
690 8.3g/cm³ 1363 darjah Lebih besar daripada atau sama dengan 485 MPa Lebih besar daripada atau sama dengan 275 MPa 25 %
718 8.2 g/cm3 1350 darjah (2460 darjah F) Psi – 135,000 , MPa – 930 Psi – 70,000 , MPa – 482 45 %
725 8.31 g/cm3 1271 darjah -1343 darjah 1137 MPa 827 MPa 20 %
X-750 8.28 g/cm3 1430 darjah 1267 MPa 868 MPa 25 %

Keluli Tahan Karat

Gred Setara Keluli Tahan Karat

STANDARD WERKSTOFF NR. UNS JIS BS GOST AFNOR EN
SS 304 1.4301 S30400 SUS 304 304S31 08Х18Н10 Z7CN18‐09 X5CrNi18-10
SS 304L 1.4306/1.4307 S30403 SUS 304L 304S11 03Х18Н11 Z3CN18–10 X2CrNi18-9 / X2CrNi19-11
SS 310 1.4845 S31000 - - - - -
SS 310S 1.4845 S31008 SUS310S - 20Ch23N18 - X8CrNi25-21
SS 316 1.4401 / 1.4436 S31600 SUS 316 316S31 / 316S33 - Z7CND17-11-02 X5CrNiMo17-12-2 / X3CrNiMo17-13-3
SS 316L 1.4404 / 1.4435 S31603 SUS 316L 316S11 / 316S13 03Ch17N14M3 / 03Ch17N14M2 Z3CND17‐11‐02 / Z3CND18‐14‐032 X2CrNiMo17-12-2 / X2CrNiMo18-14-3
SS 317 1.4449 S31700 SUS 317 - - - X6CrNiMo19-13-4
SS 317L 1.4438 S31703 SUS 317L - - - X2CrNiMo18154
SS 321 1.4541 S32100 SUS 321 - 08Ch18N10T - X6CrNiTi18-10
SS 321H 1.4541 S32109 SUS 321H - - - X6CrNiTi18-10
SS 347 1.4550 S34700 SUS 347 - 08Ch18N12B - X6CrNiNb18-10
SS 347H 1.4961 S34709 SUS 347H - - - X7CrNiNb18-10
SS 446 1.4762 S44600 - - - - -

 

Komposisi Keluli Tahan Karat

Gred C Mn Si P S Cr Mo Ni N
SS 304 0.08 maks 2 maks 0.75 maks 0.040 maks 0.030 maks 18 – 20 - 8 – 11 -
SS 304L 0.03 maks 2 maks 0.75 maks 0.045 maks 0.030 maks 18 – 20 - 8 – 12 0.10 maks
SS 310 0.25 maks 2 maks 1.50 maks 0.045 maks 0.030 maks 24 - 26 - 19 - 22 -
SS 310S 0.08 maks 2 maks 1.50 maks 0.045 maks 0.030 maks 24 - 26 - 19 - 22 -
SS 316 0.08 maks 2 maks 0.75 maks 0.045 maks 0.030 maks 16 - 18 2 - 3 10 - 14 0.1 maks
SS 316L 0.3 maks 2 maks 0.75 maks 0.045 maks 0.030 maks 16 - 18 2 - 3 10 - 14 0.10 maks
SS 317 008 maks 2 maks 1 maks 0.040 maks 0.03 maks 18 - 20 3 - 4 11 - 14 0.10 maks
SS 317L 0.035 maks 2 maks 1 maks 0.040 maks 0.03 maks 18 - 20 3 - 4 11 - 15 -
SS 321 0.08 maks 2 maks 0.75 maks 0.045 maks 0.03 maks 17 - 19 5xC min
0.60% maks		 9 - 12 0.10 maks
SS 321H 0.04 - 0.10 maks 2 maks 0.75 maks 0.045 maks 0.03 maks 17 - 19 4xC min
0.60% maks		 9 - 12 0.10 maks
SS 347 0.08 maks 2 maks 0.75 maks 0.045 maks 0.03 maks 17 - 20 10xC min
1.00 maks		 9 - 13 62.74
SS 347H 0.04 – 0.10 2 maks 0.75 maks 0.045 maks 0.03 maks 17 - 20 8xC min
1.00 maks		 9 - 13 62.74
SS 446 0.2 maks 1.5 maks 0.75 maks 0.040 maks 0.03 maks 23 – 30 0.10 – 0.25 0.50 maks Seimbang

Keluli Tahan Karat Takat Lebur, Ketumpatan dan Kekuatan Tegangan

Gred Ketumpatan Takat lebur Kekuatan Tegangan Kekuatan Hasil (0.2%Offset) Pemanjangan
SS 304 8.0 g/cm3 1400 darjah (2550 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 304L 8.0 g/cm3 1400 darjah (2550 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40 %
SS 310 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 310S 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 316 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 316L 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40 %
SS 317 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 317L 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 321 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 321H 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 347 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40 %
SS 347H 8.0 g/cm3 1454 darjah (2650 darjah F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 40 %
SS 446 7.5 g/cm3 1510 darjah (2750 darjah F) Psi – 75,000 , MPa – 485 Psi – 40,000 , MPa – 275 20 %